产品详情 //

产品性能测试：

Product performance test:

试验项目 TEST ITEM	试验方法 TEST CONDITION	试验结果 TEST RESULT
附着性 Crosshatch adhesion	1mm2方格100个，透明胶带实验 A grid of 100 squares (1mm2), peeled with a pressure sensitive tape.	100
铅笔硬度 Pencil hardness	三菱U2铅笔 MISUBISHI U2	H
耐醇性 Alcohol resistance	99.5%乙醇W=4.9N（0.5kgf）往复擦拭露底前回数 99.5% alcohol W=4.9N（0.5kgf）Calculate rubbing times before film abrading.	50回 50 time
耐水性 Water resistance	40℃×240h/浸于40℃温水中240h	无异状 No change
耐磨耗性 Abrasion resistance	（橡皮擦）W=4.9N(0.5kgf)，移行擦拭50回 (elastomer) W=4.9N(0.5kgf) ,rubbing for 50 times （干布）W=9.8N（1kgf），五块重叠，移行擦拭500回 (dry cloth) W=9.8N(1kgf), five pieces overlapping rubbing for 500 times.	不露底 No visible substrate beneath the coating
耐湿性 Humidity resistance	40℃×90%RH×240h，外观及附着性 40℃×90%RH×240h, appearance and adhesion.	无异状 No change
耐热循环 Heat cycle	（-30℃×1h→室温×1h→80℃×1h→室温×1h）5次循环，外观及附着性 （-30℃×1h→room temperature 1h→80℃×1h→room temperature 1h）×5 time, appearance and adhesion.	100

施工条件：

Construction conditions:

1.        适用底材：ABS、ABS/PC等。

1.    Applicable substrates: ABS, ABS/PC etc..

2.        测试条件：ABS塑胶板，80℃×30min干燥，放置7天后检测。

2.    Preparation of test panels:

ABS plastic panels , cure at 80℃ for 30min stay at room temperature for 7 days before test.

注意事项：

Notes:

1.        主剂使用前，应搅拌均匀，方可使用。

1.    Thoroughly mixed before use.

2.        固化剂易和空气中的水分反应，所以一定要密封，存放于阴凉干燥处。

2.    Hardener should be sealed and stored and stored in dry and cool places in case of the reaction with water.

3.        主剂/固化剂的混合比例要按标准正确测量。

3.    Exactly weight the main lacquer and hardener according to the mixed ratio.

4.        必须使用专用稀释剂稀释。

4.    Specified thinner must be used.

5.        主剂和固化剂混合后，常温下活化期限为4 小时，故应在规定的时间内用完。温度在20℃以上时，温度越高或者粘度越高，反应会随之加速，请注意。

5.    The mixture of lacquer and hardener should be used within 4 hours (RT). Above 20℃, higher temperature or higher viscosity such conditions can faster the reaction speed.